什么铜材能达到下面的要求？？

niat010113

我们有个客户需要能满足下面性能的铜材！请大家指导下
& x( L3 E. r' Z$ f" s7 H. ye-module:135*10^3Nmm^2
yield strength:490Nmm^2
tensile strength:580-680Nmm^2
请专家组提供意见

lzxh

铍铜（QBe）通过控制淬火时效工艺参数可达到上述指标。

hourpp

材料： CuNi 18 Zn 20 标准： DIN 国家与地区： Germany 金属类别： Copper Alloy 次级类别： DIN 17663 Wrought alloys

http://www.key-to-nonferrous.com/cn/img/nav/content-bgf.gif

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif

化学成分 (%) http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif ( a6 m/ Q& }, c) E" X* Z/ P6 L$ _3 x 元素 最小 最大 近似的 Cu 60.0000 63.0000 6 F% y  H, t8 B6 t. C Mn 0.7000 Zn (*) ; C: o/ ~0 K6 H + x3 M, R0 R' ~0 H$ ^ * e# |& k' B3 T5 p+ J/ d0 h( n3 w Ni 17.0000 19.0000 ' a- _; {2 c9 L1 z4 x! L Pb 0.0300 Sn ; H2 n/ v( Z4 x 0.2000 & W$ v* x5 f( }5 Q& C& c# K Fe 1 E4 V7 a9 H" d+ f7 X! I  u 0.3000 Tot. other 0.1000 / x# ?- T7 B2 }; U) ?# J 9 L6 B3 F/ ^! m) w" w& zhttp://www.key-to-nonferrous.com/cn/img/nav/spacer.gif 元素 注释 Zn Remainder

材料属性 5 R. ?# A- g" A- L& H3 {) t  oe-module:135kN/mm^2

http://www.key-to-nonferrous.com/cn/img/nav/spacer.gif

	Min.	Max.	Approx.
F 38 ; Plate, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	370	430
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	90 HB
F 38 ; Strip, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	370	430
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	90 HB
F 38 ; Tube, DIN 17671 ; <3 mm
Yield Stress, Rp0,2 (MPa):		290
Tensile Stress, Rm (MPa):	370	440
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	95 HB
F 44 ; Plate, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	430	520
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	130 HB
F 44 ; Strip, DIN 17670 ; 0.2-5 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	430	520
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	130 HB
F 53 ; Plate, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	520	610
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	155 HB
F 53 ; Strip, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	520	610
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	155 HB
F 62 ; Plate, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	540
Tensile Stress, Rm (MPa):	610
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	185 HB
F 62 ; Strip, DIN 17670 ; 0.2-2 mm
Yield Stress, Rp0,2 (MPa):	540
Tensile Stress, Rm (MPa):	610
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	185 HB
F 45 ; Tube, DIN 17671 ; <3 mm
Yield Stress, Rp0,2 (MPa):	290
Tensile Stress, Rm (MPa):	440	540
Elongation, A (%):	20
Comment:	Elongation Lo=5 mm
Hardness:	135 HB
F 55 ; Tube, DIN 17671 ; <2 mm
Yield Stress, Rp0,2 (MPa):	470
Tensile Stress, Rm (MPa):	540
Elongation, A (%):	6
Comment:	Elongation Lo=5 mm
Hardness:	160 HB
F 55 ; Rod, bars, DIN 17672 ; round 2-10 mm, polygonal 2-8 mm
Yield Stress, Rp0,2 (MPa):	440
Tensile Stress, Rm (MPa):	540	640
Elongation, A (%):	5
Comment:	Elongation Lo=5 mm
Hardness:	165 HB
F 40 ; Rod, bars, DIN 17672 ; round >=10 mm, polygonal >=8 mm
Yield Stress, Rp0,2 (MPa):		290
Tensile Stress, Rm (MPa):	390	470
Elongation, A (%):	40
Comment:	Elongation Lo=5 mm
Hardness:	95 HB
F 48 ; Rod, bars, DIN 17672 ; round 3-40 mm, polygonal 3-30 mm
Yield Stress, Rp0,2 (MPa):	340
Tensile Stress, Rm (MPa):	470	540
Elongation, A (%):	22
Comment:	Elongation Lo=5 mm
Hardness:	135 HB
F 65 ; Rod, bars, DIN 17672 ; round 1-4 mm
Yield Stress, Rp0,2 (MPa):	570
Tensile Stress, Rm (MPa):	640
Elongation, A (%):	1
Comment:	Elongation Lo=10 mm
Hardness:	190 HB

3 X. H2 V! `$ h6 L& b5 [) O
# j) G6 [2 U& q2 o[ 本帖最后由 hourpp 于 2007-12-14 13:17 编辑 ]

niat010113

请问楼上的F40是代表什么意思，我的客户要求的是F58请解释下 谢谢

hourpp

原帖由 niat010113 于 2007-12-14 13:41 发表 http://www.3dportal.cn/discuz/images/common/back.gif
9 w$ [9 a" m, h/ B1 k  t请问楼上的F40是代表什么意思，我的客户要求的是F58请解释下 谢谢

; Y6 N. C. i8 r5 \2 w8 Q" q7 i# M
% Q7 v% q7 M2 u$ Z' [2 _

F 58 ; Wire, DIN 17677 ; 0.3-0.8 mm
Tensile Stress, Rm (MPa):	620	730
Elongation, A (%):	1
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 0.8-1.5 mm
Tensile Stress, Rm (MPa):	610	710
Elongation, A (%):	2
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 1.5-3 mm
Tensile Stress, Rm (MPa):	600	690
Elongation, A (%):	3
Comment:	Elongation L0=100 mm.
F 58 ; Wire, DIN 17677 ; 3-8 mm
Tensile Stress, Rm (MPa):	580	660
Elongation, A (%):	3
Comment:	Elongation L0=100 mm.

9 [! P6 h( ]8 L: R6 U7 o3 m' I, D' a4 TF代表什么我也不知道，可能是第多少条款。

niat010113

多少是看明白了一点，不知道楼上的兄弟那里找的资料啊 ？？